440A/B/C馬氏體不銹鋼
440C是馬氏體不銹鋼的代表鋼種，可經熱處理而達到高硬度（所有不銹鋼、耐熱鋼中最高）。通常用于制造軸承、刀具，或腐蝕條件下要求高負荷、高耐磨的塑料模具。
美標中440不銹鋼有四個牌號。440A、440B、440C的含碳量依次升高；440F（ASTM A582）則在440C的基礎上加大S的含量，是一種易切削鋼種。國內對應的牌號有9Cr18、9Cr18Mo等。
>> 牌號對照
|
美國 |
ASTM |
440A |
440B |
440C |
440F |
|
UNS |
S44002 |
S44003 |
S44004 |
S44020 |
|
|
日國 |
JIS |
SUS 440A |
SUS 440B |
SUS 440C |
SUS 440F |
|
德國 |
DIN |
1.4109 |
1.4122 |
1.4125 |
— |
|
中國 |
GB |
7Cr17 |
8Cr17 |
11Cr17 9Cr18Mo |
Y11Cr17 |
>> 成分規(guī)范
|
牌號 |
440A |
440B |
440C |
440F |
9Cr18 |
9Cr18Mo |
|
C |
0.60 0.75 |
0.75 0.95 |
0.95 1.20 |
0.95 1.20 |
0.90 1.00 |
0.95 1.10 |
|
Si |
≤1.00 |
≤1.00 |
≤1.00 |
≤1.00 |
≤0.80 |
≤0.80 |
|
Mn |
≤1.00 |
≤1.00 |
≤1.00 |
≤1.25 |
≤0.80 |
≤0.80 |
|
P |
≤0.040 |
≤0.040 |
≤0.040 |
≤0.060 |
≤0.040 |
≤0.040 |
|
S |
≤0.030 |
≤0.030 |
≤0.030 |
≥0.150 |
≤0.030 |
≤0.030 |
|
Cr |
16.00 18.00 |
16.00 18.00 |
16.00 18.00 |
16.00 18.00 |
17.00 19.00 |
16.00 18.00 |
|
Mo |
≤0.75 |
≤0.75 |
≤0.75 |
— |
— |
0.40 0.70 |
|
Ni |
(≤0.50) |
(≤0.50) |
(≤0.50) |
(≤0.50) |
(≤0.60) |
(≤0.60) |
|
Cu |
(≤0.50) |
(≤0.50) |
(≤0.50) |
(≤0.60) |
— |
— |
注：括號內數(shù)值表示允許加入，并非強制要求。
>> 硬度
|
牌號 |
硬 度 |
|
|
退火態(tài)（HB） |
經過熱處理（HRC） |
|
|
440A |
≤255 |
≥54 |
|
440B |
≤255 |
≥56 |
|
440C |
≤269 |
≥58 |
|
440F |
≤269 |
≥58 |
> SUS314的卓越應用與獨特魅 ?? ? 2024-09-23
> 309si2/SUS309Si2 ?? ? 2024-09-23
> SUS347集耐蝕、耐熱、焊接 ?? ? 2024-09-23
> SUH330耐滲碳、耐熱鋼 ?? ? 2024-09-23
> SUS321：高溫與氫腐蝕的守 ?? ? 2024-09-20
> SUS310S耐熱鋼璀璨亮相 ?? ? 2024-09-20
> SUH310傲立于1035度高溫之 ?? ? 2024-09-20
上一條:H13/M2/D2模具鋼用途 下一條:CuCr與CuCrZr銅材的區(qū)別! 返回列表